landfill liners

The very best landfill liners today are made of a tough plastic film called high density polyethylene (HDPE). HDPE has only been in use in this country for this purpose since the early 1980s, so there is little actual long term experience to go on. However, landfill designers assure that HDPE resists attack by nearly all chemicals.

Resistance to chemical attack is important because the theory of landfill design says that the landfill liner must maintain its integrity for the duration of the hazard it is supposed to contain. If the garbage in the landfill will remain toxic for hundreds of years, the landfill liner must maintain its integrity for hundreds of years; if the liner fails before the hazard has gone away, the failed liner will allow the hazard to escape, and we will have simply passed today's problem onto our children and grandchildren.

When HDPE is looked up in a standard reference source (the KIRK-OTHMER ENCYCLOPEDIA OF CHEMICAL TECHNOLOGY, 3rd edition), it is learned that HDPE "is not attacked by most inorganic chemicals and is insoluble in most organic solvents at room temperature. In a study of linear polyethylene's, only 14 of 270 chemicals and materials were rated as capable of causing, upon prolonged exposure at room temperature, softening, embrittlement, or a significant loss of strength." The study cited by KIRK-OTHMER was conducted by the Phillips Petroleum Company in Bartlesville, OK,

Phillips has been in the plastic business for 30 years, and they are proud of their HDPE product. In a very informative booklet they describe the chemical properties of HDPE. The booklet described the use of HDPE for packaging. Thus the information is very relevant, because that's what a landfill liner is: a huge plastic baggie for packaging wastes; like a plastic bottle or drum, a landfill liner is intended to contain wastes, to prevent them from escaping. The booklet gave confidence that Phillips has done its homework, but it did not give confidence in HDPE as a landfill liner.

What Exactly Is A Liner?
Liners Merely Postpone Leaks

Typical Causes Of Leakage

A thick (100 mil, or 1/10 of an inch) piece of HDPE landfill liner is stiff as a linoleum tile. If chemicals make it even stiffer and it cracks under the massive weight of the garbage heaped above it, that's all she wrote for the safety of the local environment. In addition to many individual chemicals Phillips lists two major classes of chemicals that are not compatible with HDPE: aromatic hydrocarbons, and halogenated hydrocarbons. The basic aromatic hydrocarbon is benzene (a major component of gasoline); others are toluene (also called methyl benzene), and the three xylenes (o-, m-and p-xylene).

Others include naphthalene (moth balls), and pdichlorobenzene (also moth balls). These aromatic hydrocarbons "permeate excessively and cause package deformation," says Phillips.

Another class of compounds incompatible with HDPE is halogenated hydrocarbons. The most familiar names here are carbon tetrachloride, chloroform, DDT, aldrin, dieldrin, lindane, 2,4-D, 2,4,5-T, trichloroethylene, trichloroethane, perchloroethylene, and so forth. The full list is very long and growing all the time as chemists find new ways to attach chlorine, fluorine, bromine and iodine atoms to carbon and hydrogen.

The Phillips booklet lists many individual household chemicals as incompatible with HDPE.

Appendix I of the Phillips booklet lists the following chemicals under the heading "can cause stress cracks" in HDPE:

Acids: acetic acid (1% to 10% solution); aqua regia.

Foods & food products: cider, lard, margarine, vinegar, vanilla extract.

Household toiletries and pharmaceutical products: detergents (standard); detergents (heavy duty); dry cleaners; hair oil; hair shampoo; hair wave lotions; hand creams; iodine (tincture) ("embrittlement may occur after prolonged exposure"); lighter fluid; nail polish; shaving lotion; shoe polish (liquid); shoe polish (paste); soap; wax (liquid and paste); amyl alcohol 100%; carbon tetrachloride; chlorobenzene ("softening and part deformation will occur"); chloroform ("softening and part deformation will occur"); cyclohexanol; ethyl alcohol (also known as booze); methyl alcohol (a component of shellac); propyl alcohol.

Oils: castor; mineral; peppermint; vegetable; pine.

Industrial chemicals: amyl alcohol 100%; chlorobenzene; chloroform; cyclohexanol; ethyl alcohol; methyl alcohol; propyl alcohol.

So much for stress cracks. What about common chemicals that can permeate through HDPE? Phillips says "permeation is considered a physical migration of a product through the container walls." Chemicals that will permeate a plastic film will often also physically damage it. Appendix I of the Philips booklet lists the following chemicals (giving the permeation in parentheses):

Household toiletries and pharmaceutical products: lighter fluid ("high"); nail polish ("4% loss per year"); shoe polish (liquid) ("high"); turpentine ("8.5% loss per year").

Industrial chemicals: acetone ("3.4% loss per year"); amyl acetate ("4% loss per year"); amyl chloride ("high"); benzene ("high"); carbon tetrachloride ("80% loss per year"); chlorobenzene ("high; softening and part deformation will occur"); chloroform ("high"); ethylene chloride ("high; softening and part deformation will occur"); gasoline ("high"); toluene ("high; softening, swelling, and part deformation will occur"); trichloroethylene ("high; softening, swelling, and part deformation will occur").

Oils: orange ("high"); peppermint ("high"); pine ("high").

So much for chemicals that pass through HDPE, weakening it as they go.